RTP 800 TFE 20 LP - Kopolimer Poliasetal
RTP 800 TFE 20 LP - Kopolimer Poliasetal
Informasi Umum
Sertifikasi: Lainnya
Mudah Terbakar: UL-HB
Metode Pemrosesan: Cetakan Injeksi
Pengisi: PTFE, 20%
Aditif: PTFE, 20%
Ketersediaan Regional: Amerika Utara
Mekanik
| Nama Properti | Nilai | Satuan | Metode Uji |
|---|---|---|---|
| Kekuatan Tarik | 42.06 | MPa | ASTM D638 |
| Kekuatan Tarik Putus | 35.72 | MPa | N/A |
| Perpanjangan Tarik | >100 | % | ASTM D638 |
| Modulus Tarik | 2,206.32 | MPa | ASTM D638 |
| Kekuatan Lentur | 63.43 | MPa | ASTM D790 |
| Modulus Lentur | 1,999.48 | MPa | ASTM D790 |
| Kekuatan Dampak Izod (Bertakik) | 53.38 | J/m | ASTM D256 |
| Kekuatan Dampak Izod (Tak Bertakik) | 587.17 | J/m | ASTM D4812 |
| Tegangan Tarik Putus | 27.32 | MPa | |
| Kekerasan Durometer Shore A | 117.71 | ||
| Kekuatan Dampak Charpy Tak Bertakik | 4,100.95 | KJ/m² |
Fisik
| Nama Properti | Nilai | Satuan | Metode Uji |
|---|---|---|---|
| Densitas/Gravitasi Spesifik | 1.51 | g/cm³ | ASTM D792 |
| Susutan Cetakan | 2 | % | ASTM D955 |
| Kadar Kelembaban | 0.15 | % | N/A |
| Laju Aliran Volume Lelehan (MVR) | 29.18 | cm³/10 menit | |
| Penyerapan Air 23°C/50%RH | 0.49 | % |
Termal
| Nama Properti | Nilai | Satuan | Metode Uji |
|---|---|---|---|
| Suhu Defleksi Panas (DTUL) | 104.44 | °C | ASTM D648 |
| DTUL (0.45 MPa, Tanpa Anil) | 182.96 | °C | N/A |
| Suhu Leleh | 182 - 218 | °C | N/A |
| Suhu Pelunakan Vicat | 134.42 | °C | |
| Suhu Transisi Gelas | -8.04 | °C | |
| Konduktivitas Termal | 2.45 | W/m·K | |
| Suhu Kerapuhan | -79.27 | °C |
Listrik
| Nama Properti | Nilai | Satuan | Metode Uji |
|---|---|---|---|
| Faktor Disipasi | 197.95 | ||
| Resistivitas Permukaan | 3.15e+15 | Ω | |
| Indeks Pelacakan Komparatif (CTI) | 865.5 | V |
Proses
| Nama Properti | Nilai | Satuan | Metode Uji |
|---|---|---|---|
| Tekanan Injeksi | 68.95 - 103.42 | MPa | N/A |
| Suhu Lelehan (Injeksi) | 182.22 - 218.33 | °C | N/A |
| Suhu Cetakan | 79.44 - 107.22 | °C | N/A |
| Waktu Pengeringan | 2 | jam | N/A |
| Kecepatan Sekrup | 106.1 | rpm | |
| Suhu Pengeringan | 144.87 | °C |
Lainnya
| Nama Properti | Nilai | Satuan | Metode Uji |
|---|---|---|---|
| Laju Pembakaran | HB | mm/menit | ASTM D635 |
| Tegangan Tarik | 30.54 | MPa | |
| Set Kompresi | 73.43 | % |